MIL-L-87177A
TABLE II. First article testing l/
Characteristics Requirements Test method ASTM
0ryness 3.3, table I 4.6.1
Flash point 3.3, table I 01310
Grade A synthetic 3.3, table I 4.6.2 sea water
displacement
0ielectric breakdown 3.3, table I 0877
Lubricity 3.3, table I 02266 2/ Residue soluble in 3.3, table I 4.6.3
trichlorotrifluoroethane
Leakage 3.4.1.1 4.6.4
Content 3.4.1.2 4.6.5
Performance of 3.4.1.2 4.6.6 pressurized containers
Oxidation stability 3.3, table I 0942
Grade A corrosivity 3.4.3 4.6.7
Grade B corrosion 3.4.4 4.6.8 resistance
Sprayability 3.3, table I 4.6.9
Grade C shall meet all the first article testing in table II, except the corrosivity (Grade
A) and corrosion resistance (Grade B) requirements.
1/ Refer to 4.3.1
2/ Compound shall be weathered before loading into ball pot.
4.5.2 Sampling Plan B. A random sample of type I filled containers shall be selected in accordance with MIL-ST0-105, inspection level I with an AQL 2.5 percent defective from each inspection lot (see 4.3.3). The sample container(s) shall be subjected to the tests specified in table II.
4.5.3 Certification. The manufacturer shall certify that there has been no formulation or process change from that which resulted in the production of the first article inspection sample(see 4.4.2). Each ingredient material shall be identified with the name of its manufacturer and that manufacturer's trade name and formula number.
8
Source: https://assist.dla.mil -- Downloaded:
Check the source to verify that this is the current version before use.